The anodic electrophoretic paint is developed by our company on the basis of the original electrophoretic paint ED-6 according to the current market feedback, most of which have poor hand feeling and poor fingerprint resistance. Compared with the original electrophoretic paint ED-6, it not only has the original characteristics of good water solubility and high solid content. At the same time, after electrophoretic film formation, the paint film surface has better hand feeling, higher smoothness and better fingerprint resistance. In the current competitive electrophoresis industry, our company has greatly increased the market competitiveness for customers on the premise of not increasing customers' existing costs as much as possible.

II. Specifications

Item	Specification	Test Conditions
Appearance	Light yellow and clear	Visual inspection
Solid content	60±2%	105℃×3hrs
Viscosity	Z1～Z2	Gardner at 25℃
Pigment	＜2	Grander

III. Performance

Item	Performance	Test Conditions
Appearance	Flat and flawless	Visual inspection
Gloss (60℃)	120°	8μ, brown color
Hardness	3H～4H	Baking 180℃, 30 minutes, Mitsubishi pencil
Adhesion	100∕100	Paint adhesion testing
Alkali resistance	No abnormal	0.5%，NaOH 20 +/–1℃ 24 hours
Acid resistance	No abnormal	5% HCl 　 20 +/–1℃ 24 hours
Weather resistance	Retention rate 90%	QUV weather resistance test, 1000 hours
Boiling water resistance	No abnormal	95＜boiling water＜98℃　5 hours
Salt resistance	No abnormal	CASS 72 hours

At the same time, our company can provide 200KG and 50KG packing barrels according to the customer's site requirements, which is convenient for customers to store and add the paint.

The next article

Anode low-temperature curing varnish

Hone

About

Product

Performance

Case

News

Contact

High Wear-Resistant Smooth Anode Electrophoretic Paint